Type: | Oriented Silicon Steel |
---|---|
Width: | 900-1200mm |
Shape: | Coil |
Technique: | Cold Rolled |
Grade: | 23tq110 |
Standard: | GB, AISI, ASTM, DIN, BS, JIS |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Product discription
Silicon steel is an alloy formed by adding a small amount of silicon (usually below 4.5%) to pure iron, which is called silicon steel. This type of iron core has the highest saturation magnetic induction intensity value of 20000 gauss. Due to their good magnetic and electrical properties, ease of mass production, low price, and minimal mechanical stress, they have been widely used in the power electronics industry, such as power transformers, distribution transformers, current transformers, and other iron cores.
Standard Magnetic Properties | ||||||
Type | Grade | Nominal Thickness(mm) | Theoretical density(kg/dm³) |
Max core loss P/(W/kg) J=1.7T 50Hz | Min Induction J/(T) H=800A/m 50Hz | |
Conventional | 23TQ110 | 0.23 | 7.65 | 1.1 | 1.82 | |
23TQ120 | 0.23 | 7.65 | 1.2 | 1.82 | ||
27TQ120 | 0.27 | 7.65 | 1.2 | 1.82 | ||
27TQ130 | 0.27 | 7.65 | 1.3 | 1.82 | ||
30TQ120 | 0.3 | 7.65 | 1.3 | 1.82 | ||
30TQ130 | 0.3 | 7.65 | 1.3 | 1.82 | ||
35TQ145 | 0.3 | 7.65 | 1.45 | 1.82 | ||
35TQ155 | 0.3 | 7.65 | 1.55 | 1.82 | ||
High Induction | 23TQG085 | 0.23 | 7.65 | 0.85 | 1.88 | |
23TQG090 | 0.23 | 7.65 | 0.9 | 1.88 | ||
23TQG095 | 0.23 | 7.65 | 0.95 | 1.88 | ||
23TQG100 | 0.23 | 7.65 | 1 | 1.88 | ||
27TQG090 | 0.27 | 7.65 | 0.9 | 1.88 | ||
27TQG095 | 0.27 | 7.65 | 0.95 | 1.88 | ||
27TQG100 | 0.27 | 7.65 | 1 | 1.88 | ||
27TQG110 | 0.27 | 7.65 | 1.1 | 1.88 | ||
30TQG100 | 0.3 | 7.65 | 1 | 1.88 | ||
30TQG105 | 0.3 | 7.65 | 1.05 | 1.88 | ||
30TQG110 | 0.3 | 7.65 | 1.1 | 1.88 | ||
30TQG120 | 0.3 | 7.65 | 1.2 | 1.88 | ||
35TQG115 | 0.35 | 7.65 | 1.15 | 1.88 | ||
35TQG125 | 0.35 | 7.65 | 1.25 | 1.88 | ||
35TQG135 | 0.35 | 7.65 | 1.35 | 1.88 | ||
Domamin refined high induction | 23TQGR080 | 0.23 | 7.65 | 0.8 | 1.88 | |
23TQGR085 | 0.23 | 7.65 | 0.85 | 1.88 | ||
23TQGR090 | 0.23 | 7.65 | 0.9 | 1.88 | ||
23TQGR100 | 0.23 | 7.65 | 1 | 1.88 | ||
27TQGR085 | 0.27 | 7.65 | 0.85 | 1.88 | ||
27TQGR090 | 0.27 | 7.65 | 0.9 | 1.88 | ||
27TQGR095 | 0.27 | 7.65 | 0.95 | 1.88 | ||
27TQGR100 | 0.27 | 7.65 | 1 | 1.88 | ||
30TQGR095 | 0.3 | 7.65 | 0.95 | 1.88 | ||
30TQGR100 | 0.3 | 7.65 | 1 | 1.88 | ||
30TQGR110 | 0.3 | 7.65 | 1.1 | 1.88 | ||
Typical Magnetic Properties | ||||||
Type | Grade | Nominal Thickness(mm) | Theoretical density(kg/dm³) | Max core loss P/(W/kg) J=1.7T 50Hz | Min Induction J/(T) H=800A/m 50Hz | |
Conventional | 23TQ110 | 0.23 | 7.65 | 1.06 | 1.88 | |
23TQ120 | 0.23 | 7.65 | 1.15 | 1.88 | ||
27TQ120 | 0.27 | 7.65 | 1.15 | 1.87 | ||
27TQ130 | 0.27 | 7.65 | 1.25 | 1.87 | ||
30TQ120 | 0.3 | 7.65 | 1.15 | 1.87 | ||
30TQ130 | 0.3 | 7.65 | 1.25 | 1.87 | ||
35TQ145 | 0.3 | 7.65 | 1.28 | 1.86 | ||
High Induction | 23TQG085 | 0.23 | 7.65 | 0.83 | 1.91 | |
23TQG090 | 0.23 | 7.65 | 0.87 | 1.91 | ||
23TQG095 | 0.23 | 7.65 | 0.91 | 1.9 | ||
23TQG100 | 0.23 | 7.65 | 0.96 | 1.9 | ||
27TQG090 | 0.27 | 7.65 | 0.88 | 1.91 | ||
27TQG095 | 0.27 | 7.65 | 0.92 | 1.91 | ||
27TQG100 | 0.27 | 7.65 | 0.96 | 1.9 | ||
27TQG110 | 0.27 | 7.65 | 1.06 | 1.9 | ||
30TQG100 | 0.3 | 7.65 | 0.96 | 1.91 | ||
30TQG105 | 0.3 | 7.65 | 1.01 | 1.91 | ||
30TQG110 | 0.3 | 7.65 | 1.05 | 1.9 | ||
30TQG120 | 0.3 | 7.65 | 1.1 | 1.9 | ||
35TQG115 | 0.35 | 7.65 | 1.12 | 1.9 | ||
35TQG125 | 0.35 | 7.65 | 1.22 | 1.89 | ||
35TQG135 | 0.35 | 7.65 | 1.32 | 1.89 | ||
Domamin refined high induction | 23TQGR080 | 0.23 | 7.65 | 0.78 | 1.9 | |
23TQGR085 | 0.23 | 7.65 | 0.82 | 1.9 | ||
23TQGR090 | 0.23 | 7.65 | 0.86 | 1.88 | ||
23TQGR100 | 0.23 | 7.65 | 0.91 | 1.88 | ||
27TQGR085 | 0.27 | 7.65 | 0.83 | 1.9 | ||
27TQGR090 | 0.27 | 7.65 | 0.86 | 1.89 | ||
27TQGR095 | 0.27 | 7.65 | 0.91 | 1.89 | ||
27TQGR100 | 0.27 | 7.65 | 0.96 | 1.88 | ||
30TQGR095 | 0.3 | 7.65 | 0.91 | 1.9 | ||
30TQGR100 | 0.3 | 7.65 | 0.96 | 1.89 | ||
30TQGR110 | 0.3 | 7.65 | 1.03 | 1.89 | ||
Typical Mechanical | ||||||
Nominal thickness(mm) | Tensile strength (N/mm²) | Yield strength (N/mm²) | Elongation(%) | Hardness(Hv1) | Number of bends | Lamination factor(%) |
0.23 | 350 | 328 | 12 | 200 | 20 | 96.5 |
0.27 | 355 | 331 | 12 | 204 | 20 | 97 |
0.3 | 360 | 335 | 13 | 205 | 20 | 97.5 |
The firm(Shanghai) New Energy Technology Co., Ltd. is located in Shanghai, China. The firm is primarily involved in the production of cold-rolled grain-oriented silicon steel and the sale of silicon steel cores in domestic and international markets. As a manufacturing company, we can produce steel cores according to our customers' needs. In recent years, the company has established close cooperation with domestic and international new-energy transformer and generator manufacturers.
We offer a variety of products that can meet customers' multifarious demands. Our company is sincerely willing to cooperate with enterprises from all over the world in order to maintain a win-win situation and future business development.
Suppliers with verified business licenses